Zinc Rich Epoxy Primer
Zinc Rich Epoxy Primer
Type: two-part
Shades: Gray
Gloss: Matte
Chemical composition of pigment: Zinc powder with a particle size of 2 to 6 microns and a purity of 97%
Chemical composition of the resin: Polyaminoamide type epoxy resin
Percent Solid Color Weight: 65-70%
Specific gravity at 25 ° C: 2.6-2.8 g / cubic centimeter
Power coverage theory: 3-4 square meters per kilogram
Practical coverage strength: Depending on the loss factor
Film thickness: 50-70 microns
Drying time: 1 hour at 25 ° C
Full hardness time: 7 days at 25 ° C
Minimum runtime execution time: 16 hours
Maximum runtime: 72 hours
Minimum and maximum application temperature: 10-35 ° C
Usable time after mixing: 2-3 hours
Duration and storage conditions: 12 months in a cool, dry environment away from direct sunlight
The following conditions apply: The surface of the metal in accordance with the Swedish standard is sa2 1/2 sandblast.
Usage: Normal spray - airless spray - brush
Basic Features:
1 - Excellent resistance to moisture and water
2 - The second layer of coating suitable for different systems
3 - High resistance in medium to severe corrosive environments
Note: Dear customer, the above information can be changed based on your requirements and requirements. Information such as conditions of operation, atmospheric conditions, surface contamination, etc. can be useful in optimizing color formulation.
Type: two-part
Shades: Gray
Gloss: Matte
Chemical composition of pigment: Zinc powder with a particle size of 2 to 6 microns and a purity of 97%
Chemical composition of the resin: Polyaminoamide type epoxy resin
Percent Solid Color Weight: 65-70%
Specific gravity at 25 ° C: 2.6-2.8 g / cubic centimeter
Power coverage theory: 3-4 square meters per kilogram
Practical coverage strength: Depending on the loss factor
Film thickness: 50-70 microns
Drying time: 1 hour at 25 ° C
Full hardness time: 7 days at 25 ° C
Minimum runtime execution time: 16 hours
Maximum runtime: 72 hours
Minimum and maximum application temperature: 10-35 ° C
Usable time after mixing: 2-3 hours
Duration and storage conditions: 12 months in a cool, dry environment away from direct sunlight
The following conditions apply: The surface of the metal in accordance with the Swedish standard is sa2 1/2 sandblast.
Usage: Normal spray - airless spray - brush
Basic Features:
1 - Excellent resistance to moisture and water
2 - The second layer of coating suitable for different systems
3 - High resistance in medium to severe corrosive environments
Note: Dear customer, the above information can be changed based on your requirements and requirements. Information such as conditions of operation, atmospheric conditions, surface contamination, etc. can be useful in optimizing color formulation.